O1 1.2510 SKS3 9CrWMn Cold Work Die Steel Flat Bar

• Type: Steel Plate
• Standard: ASTM, AISI, GB, JIS, DIN, BS
• Certification: ISO
• Surface Treatment: Blackface
• Technique: Hot Rolled
• Application: Mold & Dies
• Model NO.: O1, 1.2510, SKS3, 9CrWMn
• Special Use: High-strength Steel Plate, Wear Resistant Steel
• Stock: Stock
• Grade: O1, 1.2510, SKS3
• Production route: Ef/Eaf+Lf+Vd/ESR
• Shape: Round Bar or Flat Steel
• Test: Ut 100% passed
• Certificate: ISO/Mill Certificate
• Lead time: 7-15 days
• Sample: Free
• MOQ: 3MT
• Steel mill: Bao Steel
• Thickness: 6-110mm
• Width: 155-610mm
• Length: 3000-6000mm
• Ut standard: Sep 1921-84 class 3 C/C to D/D
• Payment: 30% deposit, balance by L/C at sight or T/T
• Heat Treatment: Annealing or Q+T
• Transport Package: Standard or Customized
• Specification: 6-110*155-610*3000-6000mm
• Trademark: CF STEEL
• Origin: China
• HS Code: 7225400000
• Production Capacity: 1000t/Month

Product Description

O1 1.2510 SKS3 9CrWMn Cold Work Die Steel Flat Bar

Introduction
American Standard O1 special steel is not deformed oil steel, the best oil-hardened tool steel, widely used, this steel has good machining performance, stability, good wear resistance, heat resistance, dimensional deformation is small, but the toughness and corrosion resistance is weak.Commonly used in stamping die, stamping die, bending die, die, punch punch, finishing molds metal molds.
This is a very broad application of excellent steel, is used as the blade material can be processed very tough and holds an edge depth, for example Randall and Mad Dog

Standard

Chinese	American	German	Japanese
GB	AISI	DIN	JIS
9CrWMn	O1	1.2510	SKS3

Chemical Composition (%)

Grade	C	Si	Mn	P	S	V	W	Cr
1.2510	0.90-1.05	0.15-0.35	1.0-1.2	≤0.035	≤0.035	0.05-0.15	0.5-0.7	0.5-0.7
9CrWMn	0.85-0.95	≤0.4	0.9-1.2	≤0.035	≤0.035	/	0.5-0.8	0.5-0.8
O1	0.85-0.95	0.2-0.4	1.0-1.3	≤0.035	≤0.035	0.2	0.4-0.6	0.4-0.6

 

Available Size (mm)

Shape	Thickness/ Diameter	Width	Length
Flat bar	6-110	155-610	3000-6000
Round bar	14-100	/	3000-6000

Heat Treatment

Technique	Heating Temperature/ºC	Cooling	Hardness/HRC
Quenching	820-840	Oil	64-66
Tempering	160-180	Air	≥62

 

Application
1. For the overall hardened plastic mold.
2. Used to make sheet stamping touch, jewelry embossing mold
3. Used for make cold die with small cross section and complicated shape and high precision
4. For thermosetting plastic forming, it requires high wear resistance and high strength mold
5. Widely used in cutting tools, such as broaches, filament taps, long reamer, special milling cutters

Feature
(1) By oil quenching, hardness can be up to 62HRC.
(2) This Steel is not deformed oil steel and best mechanical performance , it is widely used.
(3) Higher manganese content of the steel and chromium, tungsten content, increase the hardening, the steel does not require severe water quench.
(4) The steel also better workability and wear resistance, heat treatment stable performance, small size
Deformation, but the toughness and corrosion resistance is weak.

Packing
We provide standard export packing or according to customers' request.    

Terms of payment
30% deposit T/T and the balance by L/C at sight, or T/T 100%

Delivery time
For abundant stock, 7-15 days.
For customized products, 15-30 days.

Product Show
Cold Work Die Steel Tool Steel O1, 1.2510, SKS3, 9CrWMn

Cold Work Die Steel Tool Steel O1, 1.2510, SKS3, 9CrWMn