Standard: | DIN, JIS, AISI, ASTM, GB, BS |
---|---|
Technics: | Hot Rolled |
Application: | Tool Steel Bar |
Surface: | Black |
Alloy: | Alloy |
Special Use: | High-strength Steel Plate, Wear Resistant Steel, Free Cutting Steel, Mold Steel |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Chinese | American | German | Japanese |
GB | AISI | DIN | JIS |
GCr15 | SAE52100 | 100Cr6/EN31 | SUJ2 |
Grades | C | Si | Mn | P | S | Cr | Mo | Cu | Ni |
GCr15/52100 | 0.95-1.05 | 0.15-0.35 | 0.2-0.4 | ≤0.027 | ≤0.02 | 1.3-1.65 | ≤0.1 | ≤0.25 | ≤0.3 |
100Cr6 | 0.95-1.05 | 0.15-0.35 | 0.25-0.45 | ≤0.025 | ≤0.025 | 1.4-1.65 | ≤0.08 | ≤0.25 | ≤0.3 |
Quenching | Tempering | ||||
Heating Temperature/ºC | Cooling | Hardness/HRC | Heating Temperature/ºC | Cooling | Hardness/HRC |
830-850 | Oil | 62-65 | 150-190 | Air | 58-62 |
Properties | Metric | Imperial |
Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
Elastic modulus | 190-210 GPa | 27557-30458 ksi |
Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
Hardness, Brinell | - | - |
Hardness, Knoop (converted from Rockwell C hardness) | 875 | 875 |
Hardness, Rockwell C (quenched in oil from 150°C tempered) | 62 | 62 |
Hardness, Rockwell C (quenched in water from 150°C tempered) | 64 | 64 |
Hardness, Rockwell C (quenched in oil) | 64 | 64 |
Hardness, Rockwell C (quenched in water) | 66 | 66 |
Hardness, Vickers (converted from Rockwell C hardness) | 848 | 848 |
Machinability (spheroidized annealed and cold drawn. Based on 100 machinability for AISI 1212 steel) | 40 | 40 |
Round Bar | Diameter | 16-280mm |
Length | 4000-10000mm | |
Flat Steel | Thickness | 8-200mm |
Length | 3000-4000mm |
Suppliers with verified business licenses