Technique: | Hot Rolled |
---|---|
Standard: | AISI, JIS, ASTM, DIN, GB |
Certification: | IS0, RoHS |
Ut Class: | According to Standard of Sep 1921/84, 100% Volume |
Melting Process: | Eaf+ESR |
Thickness: | 6-160mm |
Customization: |
---|
Suppliers with verified business licenses
Equivalent grades | Brief Introduction | ||||||
GB | DIN | AISI | JIS | D2 die steel, high wear resistance and micro deformation, cold working die steel, wind hard tool steel, carbon content up to 1.5%, chromium content high, noisy 11.5%, heat treatment, hardness up to 60HRC. D2 steel can be used to make large cross section, complex shape, strong impact, high resistance to cold working die steel, such as silicon steel sheet die, cold cutting scissors, trimming die, etc.. | |||
Cr12Mo1V1 | 1.2379 | D2 | SKD11 | ||||
Available size(mm) | |||||||
Flat Bar Size(mm) | Round bar Size(mm) | ||||||
Thickness | Width | Length | Diameter | Length | |||
8-80 | 155-610 | 3000-6000 | 14-80 | 300-6000 | |||
Chemical Composition(%) | |||||||
C | Si | Mn | Cr | Mo | V | P | S |
1.40-1.60 | 0.30-0.50 | 0.30-0.50 | 11.0-13.0 | 0.70-1.20 | ≤0.8 | ≤0.030 | ≤0.030 |
quench | temper | ||||||
Heating temperature/ºC | Cooling way | Hardness (HRC) | Tempering temperature /ºC |
Tempering number | Hardness (HRC) |
||
First preheating | Second preheating | Last heating | |||||
600-650 | 800-850 | 1020-1040 | Air Cooling | 61-63 | 500-560 | 2 | ≥58 |
7, Delivery condition:
EAF or ESR, Hot rolled or Forged, machined material,Annealing or Q+T
Factory Hardness: HBS=160-235.
8, Ultrasonic test standards: SEP1921-84 GR.3 CLASS D/D