Equivalent grades | Brief Introduction | ||||||
GB | DIN | AISI | JIS | D2 die steel, high wear resistance and micro deformation, cold working die steel, wind hard tool steel, carbon content up to 1.5%, chromium content high, noisy 11.5%, heat treatment, hardness up to 60HRC. D2 steel can be used to make large cross section, complex shape, strong impact, high resistance to cold working die steel, such as silicon steel sheet die, cold cutting scissors, trimming die, etc.. | |||
Cr12Mo1V1 | 1.2379 | D2 | SKD11 | ||||
Available size(mm) | |||||||
Flat Bar Size(mm) | Round bar Size(mm) | ||||||
Thickness | Width | Length | Diameter | Length | |||
8-80 | 155-610 | 3000-6000 | 14-80 | 300-6000 | |||
Chemical Composition(%) |
|||||||
C | Si | Mn | Cr | Mo | V | P | S |
1.40-1.60 | 0.30-0.50 | 0.30-0.50 | 11.0-13.0 | 0.70-1.20 | ≤0.8 | ≤0.030 | ≤0.030 |
Recommend heat treatment |
|||||||
Quenching | Tempering | ||||||
Heating temperature/ºC | Cooling way | Hardness (HRC) | Tempering temperature /ºC |
Tempering number | Hardness (HRC) |
||
First preheating | Second preheating | Last heating | |||||
600-650 | 800-850 | 1020-1040 | Air Cooling | 61-63 | 500-560 | 2 | ≥58 |
Feature | |||||||
1,Good processing, heat treatment size stability. 2,Excellent machinability. 3,Excellent dimensional stability when hardened. 4,After hardening and tempering, the high surface hardness match well with the toughness of the body. |
|||||||
Applications | |||||||
For metal stamping die, drawing die, stainless steel sheet punching die, high hardness punching die, cutting knife mold, Roll Die, metal parts production, machinery manufacturing etc. (1) Used for drawing die of refrigerator compressor rear cover, quenching hardness 56~58HRC. (2) In order to improve the service life of flat rolling material for D2 cold working die, the wear resistance and impact toughness of steel are greatly improved by adding rare earth, so as to improve the service life of flat rolling material of round die. (3) Because the content of V and Mo in D2 steel is higher than that of Cr12MoV steel, it has better comprehensive properties, and the traditional Cr12MoV steel will be replaced gradually. (4) Made of D2 steel rolling wheels, from Taiwan palette die, and Cr12MoV can improve the service life of steel compared to 5 ~6 times. |
|||||||
Terms of payment: | |||||||
30% deposit T/T and the balance by L/C at sight, or T/T | |||||||
Delivery condition: | |||||||
For abundant stock, 15-20 days.For customized products, 30-50 days. | |||||||
Factory Hardness: Soft Annealing 255HB |