Type: | Carbon Steel Bar |
---|---|
Standard: | AISI, ASTM, GB, JIS, DIN, BS |
Technique: | Hot Rolled |
Application: | Die Steel Bar |
Surface Treatment: | Polished |
Alloy: | Non-alloy |
Customization: |
---|
Suppliers with verified business licenses
EU | USA | England | Japan | China | Russia |
S235JR | A36 | 40EE | SS400 | Q235 | 17G1S |
C | Si | Mn | P | S | Cu |
0.25-0.29 | 0.28 | 1.03 | 0.04 | 0.05 | 0.2 |
Machining | The machinability rate of ASTM A36 is estimated to be 72%, and the average surface cutting feed of ASTM A36 is 120 ft/min. Machining of ASTM A36 steel is not as easy as that of AISI 1018 steel. |
Welding | ASTM A36 steel is easy to weld using any type of welding methods, and the welds and joints so formed are of excellent quality. |
Heat Treatment | Normalizing at 899°C - 954°C (1650°F-1750°F) Annealing at 843°C - 871°C(1550°F-1600°F) Stress relieving at 677°C - 927°C(1250°F-1700°F) Carburizing at 899°C - 927°C (1650°F-1700°F) Hardening at 788°C - 816°C(1450°F-1500°F) |
STANDARD/GRADE | Flat Bar Size(mm) | Round bar Size(mm) | Technics | ||||||
DIN | AISM | JIS | GB(China) | Thickness | Width | Length | Diameter | Length | |
1.2311 | P20 | PDS-3 | 3Cr2Mo | 10-700 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | Forged, Hot Rolled |
1.2738 | P20+Ni | - | 3Cr2NiMnMo | 10-1100 | 155-2200 | 2000-6000 | 20-200 | 2000-6000 | |
1.2379 | D2 | SKD10 | SKD10 | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 | |
1.2080 | D3 | SKD1 | 3Cr2Mo | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 | |
1.2083 | 420 | - | 4Cr13 | 10-500 | 155-1200 | 2000-6000 | 20-300 | 3000-6000 | |
1.2344 | H13 | SKD61 | 4Cr5MoSiV1 | 10-500 | 155-1600 | 2000-6000 | 20-400 | 3000-6000 | |
1.2510 | O1 | SKS3 | 9CrWMn | 10-200 | 155-810 | 2000-6000 | 20-200 | 3000-6000 | |
1.7225 | SAE4140 | SCM440 | 42CrMo | 10-200 | 155-2200 | 2000-6000 | 20-200 | 3000-6000 |