1.2738 718 P20+Ni Special Alloy Tool Die Mould Steel Block

• Standard: DIN, JIS, AISI, ASTM, GB, BS
• Technics: Forged
• Application: Die Steel Bar
• Surface: Black
• Alloy: Alloy
• Special Use: High-strength Steel Plate, Wear Resistant Steel, Free Cutting Steel, Mold Steel
• Model NO.: 1.2738/ P20+Ni/ 3Cr2NiMnMo/718H
• Thickness: 200-800mm
• Delivery condition: Pre-hardened HRC33-37
• Quality Assurance: 100% UT passed
• Delivery Time: 7 days
• Condition: stock
• Transport Package: Standard/Customized
• Specification: standard/customized
• Trademark: customized
• Origin: China
• HS Code: 7225
• Production Capacity: 1000 Tons/ Month

Product Description

1.2738 718 P20+Ni Special Alloy Tool Die Mould Steel Block

1. Stock Size

steel plate	Hot Rolled	Thickness	20-150mm
		Width	2200mm
		Length	2000-8000mm
	Hot Rolled	Thickness	155-300mm
		Width	1600mm
		Length	4000-8000mm
steel block	Thickness	300-1000mm
	Width	800-1600mm
	Length	2000-6000mm

2. Similar Standards

Chinese	American	German	Japanese	Swedish
GB	AISI	DIN	JIS	ASSAB
3Cr2NiMnMo	P20+Ni	1.2378	PDS5S	718

3. Chemical Composition

Grades	C	Si	Mn	P	S	Mo	Ni
1.2738	0.35-0.46	0.2-0.4	1.3-1.6	≤0.035	≤0.005	0.15-0.25	0.9-1.2
718/3Cr2NiMnMo	0.28-0.40	0.2-0.8	0.6-1.0	≤0.030	≤0.030	0.30-0.55	0.8-1.2
P20+Ni	0.32-0.40	0.2-0.4	1.0-1.5	≤0.030	≤0.035	0.30-0.55	0.8-1.2

4. Heat Treatment

Quenching			Tempering
Heating Temperature/ºC	Cooling	Hardness/HRC	Heating Temperature/ºC	Cooling	Hardness/HRC
840-870	Air	≥50	550-640	Air	28-36

5. Product Introduction
718H steel is pre-hard mirror anti-acid plastic mould steel. The steel pre-hardened, uniform material, high cleanliness, excellent polishing performance and lithography. Also has high hardenability, good electrical processing performance and striae processing performance. Pre-hardened steel without quenching can also be used for the mold bore, flange flame hardening can be implemented, the hardness can be increased to 52HRC.

6. Features
Good polishing and photo-etching properties
Good machinability
High purity and good homogeneity
Uniform hardness
No hardening risks
No hardening costs
Time saving (i.e., no waiting for heat treatment)
Lower tool cost (e.g., no distortion to rectify)
Modifications easily carried out
Can be subsequently nitrided to increase surface wear resistance and locally flame hardened to reduce surface damage.

7. Product picture