1.3243 SKH35 M35 W6MoCr4V2Co5 High Speed Alloy Tool Steel Bar

• Type: Alloy Steel Bar
• Standard: AISI, ASTM, GB, JIS, DIN, BS
• Technique: Hot Rolled
• Application: Tool Steel Bar
• Surface Treatment: Black Surface
• Alloy: Alloy
• Model NO.: M35/W6MoCr4V2Co5/1.3243/SKH35
• Special Use: Free Cutting Steel
• Test: SGS / Ut 100% / Element Testing
• Payment: 30% Deposit,Blance by L/C at Sight or T/T
• Certificate: ISO/Mill Certificate
• Delivery Handness: Hb<=285
• Transport Package: Normal Package&Customers′ Demand
• Specification: According to customer requirements
• Trademark: CF STEEL
• Origin: China
• HS Code: 7228300000
• Production Capacity: 1000mt/Month

Product Description

High Speed Alloy Tool Steel Bar (M35/W6MoCr4V2Co5/1.3243/SKH35)

Features:
(1),For tungsten molybdenum containing cobalt high speed steel, improve the red hardness and high temperature hardness;
(2),Improved wear resistance, good machinability, but lower strength and impact toughness, easy oxidation decarburization;
(3),Commonly used for gear cutting tools, milling tools and tools such as punch, cutter for cutting hard material;

Application:
(1)Has good machinability, but lower strength and impact toughness;
(2)easy oxidation decarburization, commonly used for gear cutting tools, milling tools and tools such as punch,;
(3)cutter for cutting hard material;

Chemical composition %:

C	Si	Mn	S	P	Cr	Ni	Cu	V	Mo	W	Co
0.80~0.90	0.20~0.45	0.15~0.40	≤0.030	≤0.030	3.75~4.50	≤0.30	≤0.25	1.75~2.25	4.50~5.50	5.50~6.50	4.50~5.50

Size:Flat Bars(mm):
Thickness:20-400  Width:200-800  Length:1000~6000     Round Bar (mm):Φ20~400

Mechanical property:
Hardness:≥64HRC

Heat treatment
Preheat:1190~1210ºC or 1200~1220ºC heating,oil cooling:540~560ºC
Tempering:Twice,2hours each time.

Delivery status: Hot rolled,forged,annealed,

Surface conditions: Rough turning, peeling, polishing

Delivery hardness: ≤285HB;Annealed ≤269HB    quenching:730~840ºC

Quality Contation of our steel products
1)Both end of each bar must be cut
2)Ladle furnanced and vacuum de-gassed
3)Show heat No. on each bar
4)Surface condition the surface of the hot rolled square bar shall befree cracks, scar and wrinkles that affect the use of the billets. In case there is the above-mentioned defect, it shall be remove.
5)The mill test certificate shall show the chemical composition, and it is guaranteed that the chemical composition shall be within the limit stipulated in the contract.

Product pictures: